| BA-U- Aramide Fibres, Nitrile
General Properties & Application:
- Good Chemical, mechanical & thermal properties
- General use
Approvals:
- DIN-DVGW (DIN 3535/6)
- SVGW (DIN 3535/6)
- SVGW (W/TPW)
- HTB (DVGW VP 401)
- DVGW KTW
- DVGW W270
- WQc/WRAS
- BAM (Oxygen)
- Germanischer Lloyd
- CRS - Croatian Register of Shipping
- BS 7531 Grade Y
- TA-Luft (VDI 2440)
|
| Technical Data |
| Compressibility
|
8% |
| Recovery
|
55% |
| Tensile Strength
|
11 MPa |
| Stress Resistence |
| 16h, 300°C, 50 | 22 MPa |
| 16h, 175°C, 50 | 28 MPa |
| Specific Leak Rate
|
0.05 mg/(s-m) |
| Thickness Increase |
| ASTM Fuel B, 5h, 20°C
|
5% |
| Oil IRM 903, 5h, 150°C
|
5% |
| Max. Operating Conditions |
| Peak Temperature
|
350°C/662°F |
| Continuous Temperature |
250°C/482°F |
| - with steam
|
200°C/392°F |
| Pressure |
100bar/1450psi |
|
 |
BA-50- Aramide Fibres, Nitrile
General Properties & Application:
- Gasket material with good chemical resistance.
Very suitable for higher loading
- Gas, food, chemical industry
Approvals:
- DIN-DVGW (DIN 3535/6)
- SVGW (DIN 3535/6)
- SVGW (W/TPW)
- DVGW KTW
- WQc/WRAS
- Germanischer Lloyd
- CRS - Croatian Register of Shipping
- TA-Luft (VDI 2440)
|
| Technical Data |
| Compressibility
|
8% |
| Recovery
|
45% |
| Tensile Strength
|
9 MPa |
| Stress Resistence |
| 16h, 300°C, 50 | 20 MPa |
| 16h, 175°C, 50 | 25 MPa |
| Specific Leak Rate
|
0.08 mg/(s-m) |
| Thickness Increase |
| ASTM Fuel B, 5h, 20°C
|
10% |
| Oil IRM 903, 5h, 150°C
|
10% |
| Max. Operating Conditions |
| Peak Temperature
|
280°C/536°F |
| Continuous Temperature |
220°C/428°F |
| - with steam
|
180°C/356°F |
| Pressure |
80bar/1160psi |
|
 |
BA-CF- Carbon Fibres, Nitrile
General Properties & Application:
- Material with excellent resistance to steam and
strong alkaline media
- Chemical and petrochemical industry
Approvals:
- DIN-DVGW (DIN 3535/6)
- SVGW (DIN 3535/6)
- HTB (DVGW VP 401)
- DVGW KTW
- BAM (Oxygen)
- CRS - Croatian Register of Shipping
- BS 7531 Grade Y
- BS 7531 Grade X
|
| Technical Data |
| Compressibility
|
9% |
| Recovery
|
55% |
| Tensile Strength
|
8 MPa |
| Stress Resistence |
| 16h, 300°C, 50 | 25 MPa |
| 16h, 175°C, 50 | 30 MPa |
| Specific Leak Rate
|
0.05 mg/(s-m) |
| Thickness Increase |
| Oil IRM 903, 5h, 150°C
|
7% |
| Max. Operating Conditions |
| Peak Temperature
|
400°C/752°F |
| Continuous Temperature |
300°C/572°F |
| - with steam
|
280°C/536°F |
| Pressure |
100bar/1450psi |
|
 |
BACF-4000- Carbon Fibre, Nitrile
General Properties & Application:
- Environment friendly gasket material w/enhanced
resistance to steam & strong alkaline media.
Corres-
ponds to TA Luft
- Chemical, pulp, & paper industry; saturated
steam distribution
Approvals:
- DIN-DVGW (DIN 3535/6)
- HTB (DVGW VP 401)
- TARC/MRPRA
- TA Luft (VDI 2440)
- BS 7531 Grade X
Top of Page |
| Technical Data |
| Density
|
1.5-1.7 g/m3 |
| Compressibility
|
9% |
| Recovery
|
55% |
| Tensile Strength
|
8 MPa |
| Stress Resistence |
| 16h, 300°C, 50 | 25 MPa |
| 16h, 175°C, 50 | 30 MPa |
| Specific Leak Rate
|
0.05 mg/(s-m) |
| Thickness Increase |
| ASTM Fuel B, 5h, 20°C
|
≤5% |
| Oil IRM 903, 5h, 150°C
|
7% |
| Specific Leakage Rate
|
≈0.10 mg/(s-m) |
| Compression Modulus |
| At Room Temperature εKSW
|
>3.5% |
| At Elevated Temperature εKSW/200°C
|
7% |
| Recover R
|
≈0.026 mm |
| Max. Operating Conditions |
| Peak Temperature
|
440°C/824°F |
| Continuous Temperature |
350°C/662°F |
| - with steam
|
280°C/536°F |
| Pressure |
120bar/1740psi |
|